TOSOH Zirconia-Beads
Suitable for wet grinding and dispersing applications, including the processing of highly viscous materials.
- Higher density – a greater impact force resulting in superior grinding efficiency
- Smooth surface, ideal roundness/sphericity and narrow size distribution – higher productivity grinding and dispersion
- Higher wear resistance -minimizing product contamination from media wear
- Resistant to rust and corrosion – compatible with water based processing
| Item | |
|---|---|
| Chemical composition | ZrO2, Y2O3 |
| Density (g/cm3) | 6.0 |
| Hardness | 1250 HVIO |
| Modulus of elasticity | 210 GPa |
| Bending Strength | 1200 MPa |
| Diameter (φ,mm) | Tolerance (mm) | Filling Density (kg/L) |
| 0.03 | 0.02 | 3.5 |
| 0.03 | -0.015 | 3.5 |
| 0.05 | 0.03 | 3.55 |
| 0.05 | -0.02 | 3.55 |
| 0.1 | 0.03 | 3.7 |
| 0.1 | -0.02 | 3.7 |
| 0.2 | 0.07 | 3.7 |
| 0.2 | -0.03 | 3.7 |
| 0.3 | 0.07 | 3.9 |
| 0.3 | -0.01 | 3.9 |
| 0.4 | 0.1 | 3.9 |
| 0.4 | -0.05 | 3.9 |
| 0.5 | 0.15 -0.1 | 3.9 |
| 0.65 | 0.15 -0.1 | 3.8 |
| 0.8 | 0.15 -0.1 | 3.8 |
| 1 | ±0.15 | 3.8 |
| 1.25 | ±0.15 | 3.8 |
| 1.5 | ±0.15 | 3.8 |
| 1.75 | ±0.15 | 3.7 |
| 2 | ±0.15 | 3.7 |
| 2.3 | ±0.15 | 3.7 |
| 2.7 | ±0.2 | 3.7 |
| 3 | ±0.2 | 3.7 |
| 4 | ±0.3 | 3.6 |
| 5 | ±0.3 | 3.6 |
| 10 | ±1.0 | 3.5 |
| 15 | ±1.0 | 3.4 |
| 20 | ±1.0 | 3.3 |
| 25 | ±1.0 | 3.2 |
Paints and coatings / Printing inks / Pigments and dyes / Automobile coatings / Dielectric, piezoelectric and magnetic materials / Agrochemicals / Nano paste / Electronic Paste / Battery and fluorescent materials / Conductive materials / Ceramic inks / Biomaterials / Metal oxides / Pharmaceutical, dental, cosmetic, and foodstuffs