TOSOH Zirconia-Beads
Suitable for wet grinding and dispersing applications, including the processing of highly viscous materials.
- Higher density – a greater impact force resulting in superior grinding efficiency
- Smooth surface, ideal roundness/sphericity and narrow size distribution – higher productivity grinding and dispersion
- Higher wear resistance -minimizing product contamination from media wear
- Resistant to rust and corrosion – compatible with water based processing
| Item | |
|---|---|
| Chemical composition | ZrO₂(95%)+Y₂O₃(5%) |
| Density (g/cm3) | 6.0 |
| Hardness | 1250 HVIO |
| Modulus of elasticity | 210 GPa |
| Bending Strength | 1200 MPa |
| Fracture toughness | 6.0 MPa√m |
| Diameter (φ,mm) | Tolerance (mm) | Filling Density(kg/L) |
| 0.03 | 0.02 | 3.5 |
| -0.015 | ||
| 0.05 | 0.03 | 3.55 |
| -0.02 | ||
| 0.1 | 0.03 | 3.7 |
| -0.02 | ||
| 0.2 | 0.07 | |
| -0.03 | ||
| 0.3 | 0.07 | 3.9 |
| -0.01 | ||
| 0.4 | 0.1 | |
| -0.05 | ||
| 0.5 | 0.15 -0.1 | |
| 0.65 | 3.8 | |
| 0.8 | ||
| 1 | ±0.15 | |
| 1.25 | ||
| 1.5 | ||
| 1.75 | 3.7 | |
| 2 | ||
| 2.3 | ||
| 2.7 | ±0.2 | |
| 3 | ||
| 4 | ±0.3 | 3.6 |
| 5 | ||
| 10 | ±1.0 | 3.5 |
| 15 | 3.4 | |
| 20 | 3.3 | |
| 25 | 3.2 |
Paints and coatings | Printing inks | Pigments and dyes | Automobile coatings | Piezoelectric and magnetic materials |
Nano paste | Electronic Paste | Battery and fluorescent materials | Conductive materials | Ceramic inks |
Metal oxides | Pharmaceutical | Dental | Cosmetic | foodstuffs |
Agrochemicals | Biomaterials | Dielectric |
|
|